SABIC Innovative Plastics Lexan? FXD141R PC (Europe-Africa-Middle East)
Polymer,Thermoplastic,Polycarbonate (PC)SABIC Innovative Plastics (GE Plastics)产品说明:LEXAN FXD141R is a transparent/translucent medium viscosity grade for light diffusion effects. Internal mold release. The color package may affect performance.
SABIC Innovative Plastics Lexan? FXD141R PC (Europe-Africa-Middle East) 物性表
物理性能额定值 (公制)额定值 (英制)测试方法密度 | 1.20 g/cc | 0.0434 lb/in? | ISO 1183 |
水分吸收 | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
饱和吸水率 | 0.35 % | 0.35 % | ISO 62 |
线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
化合物熔体指数 | 11 g/10 min @Load 1.20 kg, Temperature 300 °C | 11 g/10 min @Load 2.65 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 |
硬度,H358/30 | 95.0 MPa | 13800 psi | ISO 2039-1 |
抗张强度(断裂) | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
抗张强度(屈服) | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
伸长率 (断裂) | 110 % | 110 % | 50 mm/min; ISO 527 |
屈服伸长率 | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
拉伸模量 | 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 |
弯曲强度 | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
弯曲模量 | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
悬壁梁缺口冲击强度 | 70.0 kJ/m? | 33.3 ft-lb/in? | 80*10*3; ISO 180/1A |
12.0 kJ/m? @Temperature -30.0 °C | 5.71 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
悬壁梁无缺口冲击强度 | NB | NB | 80*10*3; ISO 180/1U |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
简支梁无缺口冲击强度 | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
NB @Temperature -30.0 °C | Edgew 80*10*3 sp=62mm; ISO 179/1eU | ||
简支梁缺口冲击强度 | 7.30 J/cm? | 34.7 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
1.40 J/cm? @Temperature -30.0 °C | 6.66 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
体积电阻率 | >= 1.00e+15 ohm-cm |