PC 美国液氮 DFL14

SABIC Innovative Plastics LNP LUBRICOMP DFL14 PCPolymer,Thermoplastic,Polycarbonate (PC)SABIC Innovative Plastics (GE Plastics)产品说明:LNP LUBRICOMP* DFL14 is a compound based on Polycarbonate resin containing 20% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated.SABIC Innovative Plastics LNP LUBRICOMP DFL14 PC 物性表物理性能额定值 (公制)额定值 (英制)测试方法比重1.38 g/cc1.38 g/ccASTM D792密度1.38 g/cc0.0499 lb/in?ASTM D792水分吸收0.120 %0.120 %50% RH, 24 hrs; ASTM D5700.190 %0.190 %23°C / 50% RH; ISO 62线性成型收缩率,Flow0.0020 - 0.0040 cm/cm@Time 86400 sec0.0020 - 0.0040 in/in@Time 24.0 hourASTM D955线性成型收缩率，横向0.0050 - 0.0070 cm/cm@Time 86400 sec0.0050 - 0.0070 in/in@Time 24.0 hourASTM D955机械性能额定值 (公制)额定值 (英制)测试方法抗张强度(断裂)94.0 MPa13600 psiType I, 5 mm/min; ASTM D63894.0 MPa13600 psi5 mm/min; ISO 527抗张强度(屈服)96.0 MPa13900 psiType I, 5 mm/min; ASTM D63896.0 MPa13900 psi5 mm/min; ISO 527伸长率 (断裂)3.5 %3.5 %5 mm/min; ISO 5273.8 %3.8 %Type I, 5 mm/min; ASTM D638屈服伸长率2.9 %2.9 %5 mm/min; ISO 5273.0 %3.0 %Type I, 5 mm/min; ASTM D638拉伸模量6.02 GPa873 ksi1 mm/min; ISO 5276.32 GPa917 ksi5 mm/min; ASTM D638弯曲强度158 MPa22900 psiISO 178161 MPa23400 psi1.3 mm/min, 50 mm span; ASTM D790165 MPa23900 psi1.3 mm/min, 50 mm span; ASTM D790弯曲模量5.59 GPa811 ksi2 mm/min; ISO 1785.82 GPa844 ksi1.3 mm/min, 50 mm span; ASTM D790悬壁梁缺口冲击强度1.70 J/cm3.18 ft-lb/inASTM D256悬壁梁无缺口冲击强度7.16 J/cm13.4 ft-lb/inASTM D4812悬壁梁缺口冲击强度15.0 kJ/m?7.14 ft-lb/in?80*10*4; ISO 180/1A悬壁梁无缺口冲击强度54.0 kJ/m?